Abstract Plastic deformation in body-centred cubic (bcc) metals and alloys is conventionally mediated by screw dislocations. Their temperature-sensitive motion is attributed to a steep rise in strength with decreasing temperature that constricts plastic zones at crack tips, leading to a ductile-to-brittle transition1.