1 Introduction The clarification of the fundamental laws of the optimal glass-forming compositions in multicomponent alloys has been a pivotal challenge in the field of metallic glasses (MGs) [1-8]. Traditionally, compositions adjacent to the eutectic points of phase diagrams have been regarded as ideal candidates for glass formation due to their suppressed crystallization tendency and low liquidus temperatures [9, 10].